硅胶手板模型是重要的一种手板材料，很多产品中都需要用到硅胶产品。那么硅胶手板模型加工注意事项有那些呢？手板模型加工有气泡、粘模及变形怎么处理呢？

Silicone hand model is an important hand material, and silicone products are needed in many products. So what are the precautions for silicone hand mold processing? How to deal with bubbles, mold sticking and deformation in the processing of hand model?

1、模具硅胶里有很多气泡

1. There are many bubbles in the silicone of the mold

这种情况要依据条件来处里，在有抽真空机的条件下，先要把硅胶与固化剂搅拌均匀后进行抽真空处理。如没有真空机则可以适当减少固化剂的添加量来进行处理，比如原硅胶与固化剂的比率为4%,现在可以改成1%-2%。这样前期模具硅胶胶连时间就会变慢，模具中的空气就会慢慢排出，减少气泡。

This situation should be handled according to the conditions. Under the condition of vacuum pumping machine, the silica gel and curing agent should be stirred evenly before vacuum pumping. If there is no vacuum machine, the amount of curing agent can be appropriately reduced for treatment. For example, the ratio of original silica gel to curing agent is 4%, and now it can be changed to 1% - 2%. In this way, the silica gel bonding time of the early mold will slow down, and the air in the mold will be slowly discharged to reduce bubbles.

2、硅胶出现粘模

2. Silicone sticking

出现这种情况一是因为前期对模种（产品模型）没有合理处理造成的，所以在开模前要对模种进行处理，如模种表面比较粗燥或做很复杂的模具，一定要认真打磨光滑清洗干净。然后再均匀刷上脱模剂。常用的脱模剂有凡士林、洗洁精、液体石蜡等。实际操作中可根据模种的材质涂刷不同的脱模剂。二是固化剂搅拌不均匀就倒入模具框中，脱模时一块干一块不干。

One reason for this is that there is no reasonable treatment of the mold type (product model) in the early stage, so the mold type should be treated before opening the mold. If the surface of the mold type is rough and dry or a very complex mold is made, it must be carefully polished and cleaned. Then apply the release agent evenly. Common mold release agents include Vaseline, detergent, liquid paraffin, etc. In practice, different release agents can be applied according to the material of the mold. Second, the curing agent is poured into the mold frame if it is not stirred evenly, and it will be dried one by one during demoulding.

3、硅胶模具产品变形

3. Silicone mold product deformation

济南手板厂家认为这个要依据产品的大小来分开处理，原则上是产品的大小尺寸与所使用硅胶的硬度成正比。若是小件产品或非常精细的产品可以使用很软的硅胶来开模，硬度一般在10-20度，这样会好脱模，还不会破坏精细产品的纹路。

Jinan hand board manufacturers believe that this should be handled separately according to the size of the product. In principle, the size of the product is directly proportional to the hardness of the silicone used. For small products or very fine products, very soft silica gel can be used to open the mold, and the hardness is generally 10-20 degrees, which will facilitate demoulding and will not damage the lines of fine products.

若是大件产品比如大于50公分的产品就一定要使用硬度为40-50的硅胶来开模。这样才不会变形。若是做很大而且又很精细的产品可以使用硬度为30度左右的硅胶来开模（方法是刷一层硅胶蒙上一层玻璃纤维布再刷一层硅胶），外面可以用石膏，玻璃钢（即不饱和树脂+玻璃纤维布）来做外膜，以此来保护的产品不变形。

For large products, such as products larger than 50 cm, silicone with a hardness of 40-50 must be used to open the mold. This will not deform. For large and fine products, you can use silica gel with a hardness of about 30 degrees to open the mold (by brushing a layer of silica gel, covering it with a layer of glass fiber cloth, and then brushing a layer of silica gel). Gypsum and glass fiber reinforced plastic (that is, unsaturated resin + glass fiber cloth) can be used as the outer film to protect the product from deformation.

以上就是问题解答的相关内容了，希望能够帮助到大家，如对这一问题还存在任何疑问，都欢迎关注我们网站http://m.axcwv.cn并咨询我们的工作人员，将竭诚为您服务。

The above is the relevant content of the question answer. I hope it can help you. If you still have any questions about this problem, you are welcome to follow our website http://m.axcwv.cn And consult our staff, will serve you wholeheartedly.